High density calcium silicate board 980 kg/m³ thermal shock resistant grade. Compressive strength ≥15 MPa, flexural strength ≥7.0 MPa, designed to withstand rapid temperature cycling without cracking or degradation. Linear shrinkage only 0.2% at 850°C.
This is the thermal shock resistant grade high density calcium silicate board, specifically designed for applications involving rapid temperature cycling and extreme thermal stress.
With a density of 980 kg/m³, compressive strength of ≥15 MPa and flexural strength of ≥7.0 MPa, this product maintains structural integrity under repeated thermal shock conditions.
The thermal shock grade offers excellent resistance to cracking and degradation during rapid heating and cooling cycles, making it ideal for furnace linings, kiln furniture and other applications with severe temperature fluctuations.
Dimensioni Standard: 1230 × 1230 mm, thickness 6–160 mm; 1250 × 2500 mm, thickness 10–80 mm; 1200 × 600 mm, thickness 10–160 mm (custom sizes and shaped products available)
High density calcium silicate board 980kg/m³ thermal shock grade — manufactured by HR RHINO
High Density Calcium Silicate Board Shock Termico Grade, density: 980 kg/m³
| SiO₂ | % | 50 Min |
| CaO | % | 35 Min |
| Al₂O₃ | % | 1 Max |
| Fe₂O₃ | % | 0.5 Max |
| Loss on Ignition | % | 7 Max |
| Applicazione Grade | Shock Termico | |
| Densità Apparente | kg/m³ | 980 |
| Resistenza a Compressione | MPa | ≥ 15 |
| Resistenza a Flessione | MPa | ≥ 7.0 |
| Temp. Max Servizioerature | °C | 1000 |
| Conducibilità Termica (400°C) | W/m·K | ≤ 0.14 |
| Conducibilità Termica (800°C) | W/m·K | ≤ 0.22 |
| Ritiro Lineare (850°C, 3h) | % | ≤ 0.2 |
| Lunghezza mm (±2mm) | Larghezza mm (±2mm) | Spessore mm (±2mm) |
| 1230 | 1230 | 6–160 |
| 1250 | 2500 | 10–80 |
| 1200 | 600 | 10–160 |