High density calcium silicate board 850 kg/m³ N-14 grade with excellent compressive strength ≥14 MPa, flexural strength ≥6.1 MPa, low thermal conductivity and good dimensional stability with only 0.3% shrinkage at 850°C. Ideal para structural insulation applications.
This is the N-14 grade high density calcium silicate board designed for structural insulation applications requiring excellent compressive strength and thermal performance.
With a density of 850 kg/m³, compressive strength of ≥14 MPa and flexural strength of ≥6.1 MPa, this product provides reliable structural support combined with superior thermal insulation.
The N-14 grade offers an ideal balance between mechanical strength, thermal conductivity and dimensional stability for demanding industrial environments.
Tamaño Estándar: 1230 × 1230 mm, thickness 6–160 mm; 1250 × 2500 mm, thickness 10–80 mm; 1200 × 600 mm, thickness 10–160 mm (custom sizes and shaped products available)
High density calcium silicate board 850kg/m³ N-14 grade — manufactured by HR RHINO
High Density Calcium Silicate Board Grado N-14, density: 850 kg/m³
| SiO₂ | % | 50 Min |
| CaO | % | 35 Min |
| Al₂O₃ | % | 1 Max |
| Fe₂O₃ | % | 0.5 Max |
| Loss on Ignition | % | 7 Max |
| Aplicación Grade | N-14 | |
| Densidad Aparente | kg/m³ | 850 |
| Resistencia a Compresión | MPa | ≥ 14 |
| Resistencia a Flexión | MPa | ≥ 6.1 |
| Temp. Máx. Servicioerature | °C | 1000 |
| Conductividad Térmica (400°C) | W/m·K | ≤ 0.11 |
| Conductividad Térmica (800°C) | W/m·K | ≤ 0.16 |
| Contracción Lineal (850°C, 3h) | % | ≤ 0.3 |
| Longitud mm (±2mm) | Ancho mm (±2mm) | Espesor mm (±2mm) |
| 1230 | 1230 | 6–160 |
| 1250 | 2500 | 10–80 |
| 1200 | 600 | 10–160 |